玻璃纤维增强材料15%,抗冻, 抗溶剂性, 耐疲劳性能, 流动性高, 齿轮,汽车的发动机罩下的零件, 动力/其它工具, 外壳

 

Vydyne® R515H Natural

聚酰胺66

Ascend Performance Materials Operations LLC

Technical Data

 

产品说明

 

Vydyne R515H Natural is high-flow, heat-stabilized, hydrolysis-resistant, 15% glass-fiber reinforced PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is also lubricated for improved flow and offers superior surface appearance.

 

Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep, and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.

 

Vydyne R515H Natural is heat-stabilized to minimize oxidative degradation of the polymer when exposed to elevated temperatures in service. This product provides improved retention of physical properties under exposure to long-term heat. Also, Vydyne R515H Natural has excellent knit-line strength and fatigue resistance, which is essential for cycle testing with anti-freeze solutions.

 

Typical Applications/End Uses:

Vydyne R515H Natural is successfully used in a wide range of injection molding engineering applications, including automotive clips, radiator end tanks, parts of the air-conditioning and petrol distribution system, etc. (under the hood); electrical connectors, housings, bobbins, etc.; and in industrial applications such as gears, bearing shells, covers, housings, etc.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet

UL 黄卡 2 •  E70062-249083

搜索 UL 黄卡 •  Ascend Performance Materials Operations LLC

•  Vydyne®

供货地区 • 北美洲 • 欧洲 • 亚太地区

填料/增强材料 • 玻璃纤维增强材料, 15% 填料按重量

添加剂 • 热稳定剂 • 润滑剂

• 刚性，高 • 耐化学性良好 • 热稳定性

• 高强度 • 耐汽油性

特性 • 润滑

• 抗溶剂性 • 耐油性能

• 脱模性能良好

• 流动性高 • 耐油脂性能

用途 • 齿轮 • 汽车的发动机罩下的零件

• 动力/其它工具 • 外壳

机构评级 • ASTM D 4066 PA0121G15 • ASTM D 6779 PA0121G15

UL文件号 • E70062

外观 • 自然色

形式 • 粒子

加工方法 • 注射成型

物理性能 干燥 调节后的 单位制 测试方法

密度 1.24 -- g/cm³ ISO 1183

收缩率 ISO 294-4

垂直流动方向 : 23°C, 2.00 mm 1.0 -- %

流动方向 : 23°C, 2.00 mm 0.50 -- %

吸水率 ISO 62

23°C, 24 hr 1.0 -- %

平衡, 23°C, 50% RH 2.2 -- %

机械性能 干燥 调节后的 单位制 测试方法

拉伸模量 (23°C) 6600 4000 MPa ISO 527-2

拉伸应力 (断裂, 23°C) 120 80.0 MPa ISO 527-2

拉伸应变 (断裂, 23°C) 3.0 13 % ISO 527-2

弯曲模量 (23°C) 5900 3250 MPa ISO 178

弯曲应力 (23°C) 170 110 MPa ISO 178

泊松比 0.40 -- ISO 527-2

 

Vydyne® R515H Natural

聚酰胺66

Ascend Performance Materials Operations LLC

冲击性能 干燥 调节后的 单位制 测试方法

简支梁缺口冲击强度 ISO 179

-30°C 6.0 5.3 kJ/m²

23°C 6.0 7.5 kJ/m²

简支梁无缺口冲击强度 ISO 179

-30°C 32 38 kJ/m²

23°C 39 43 kJ/m²

悬壁梁缺口冲击强度 ISO 180

-30°C 5.7 5.4 kJ/m²

23°C 6.6 7.0 kJ/m²

热性能 干燥 调节后的 单位制 测试方法

热变形温度

0.45 MPa, 未退火 258 -- °C ISO 75-2/B

1.8 MPa, 未退火 241 -- °C ISO 75-2/A

熔融温度 260 -- °C ISO 11357-3

线形热膨胀系数 ISO 11359-2

流动 : 23 到 55°C, 2.00 mm 3.0E-5 -- cm/cm/°C

横向 : 23 到 55°C, 2.00 mm 1.1E-4 -- cm/cm/°C

RTI Elec UL 746

0.750 mm 140 -- °C

1.50 mm 140 -- °C

3.00 mm 140 -- °C

RTI Imp UL 746

0.750 mm 120 -- °C

1.50 mm 120 -- °C

3.00 mm 120 -- °C

RTI UL 746

0.750 mm 125 -- °C

1.50 mm 140 -- °C

3.00 mm 140 -- °C

电气性能 干燥 调节后的 单位制 测试方法

体积电阻率 (0.750 mm) 1.0E+13 -- ohm•cm IEC 60093

介电强度 (1.00 mm) 20 -- kV/mm IEC 60243

耐电弧性 (3.00 mm) PLC 6 -- ASTM D495

漏电起痕指数 (3.00 mm) 250 到 399 -- V IEC 60112

高电弧燃烧指数(HAI) UL 746

0.750 mm PLC 0 --

1.50 mm PLC 0 --

3.00 mm PLC 0 --

高电压电弧起痕速率 (HVTR) PLC 1 -- UL 746

热丝引燃 (HWI) UL 746

0.750 mm PLC 4 --

1.50 mm PLC 3 --

3.00 mm PLC 4 --

可燃性 干燥 调节后的 单位制 测试方法

UL 阻燃等级 UL 94

0.750 mm HB --

1.50 mm HB --

3.00 mm HB --

灼热丝易燃指数 IEC 60695-2-12

0.750 mm 675 -- °C

1.50 mm 675 -- °C

3.00 mm 675 -- °C

 

Vydyne® R515H Natural

聚酰胺66

Ascend Performance Materials Operations LLC

可燃性 干燥 调节后的 单位制   测试方法

热灯丝点火温度 IEC 60695-2-13

0.750 mm 700 -- °C

1.50 mm 700 -- °C

3.00 mm 700 -- °C

注射 干燥单位制

干燥温度 80.0°C

干燥时间 4.0hr

建议的最大回制料比例 25%

料筒后部温度 280 到 310°C

料筒中部温度 280 到 310°C

料筒前部温度 280 到 310°C

射嘴温度 280 到 310°C

加工（熔体）温度 285 到 305°C

模具温度 65.0 到 95.0°C

 

 

 

 

 

 